High Pressure Drilling Mud Pumps Ceramic Liner drilling rig tools
Description:
- HYRD Petroleum Technology Co., Ltd. ,which has passed ISO9001 Authentication, specializes to research, develop and manufacture the Mud Pump and its expendable parts and its technology & quality control are in line with API Spec 7K Standard.
The Products can be supplied:
Liner
Liner is divided into Ceramic Sleeve Liner, Double Metal Liner, Carburization & quenching Liner and Chrome-plated Liner
a.) Ceramic Sleeve Liner
Material of sleeve is Zirconia and its shell is 45#(ASTM1045)forged steel.
1 . Mud Pump:
8P-80,9P-100,10P-130,12P-160,F-500,F-800,F-1000,F-1300,F-1600,PZ-7,PZ-9,PAH,TEE,W-440,W-446,3NB350,3NB-500C,3NB-800C,3NB-1000C,3NB-1300C,3NB-1600
2. Plunger Pump:
TWS600S,TWS2000,DOWILL300,HyT-400.
3. Skid- mounted & Pump Unit for each kinds of pump said above.
4. Spare Parts and Expendable parts: With the specialized & batched production liner, we can supply power end assembly, fluid end assembly and its spare parts, which can be easily matched & exchanged with some international famous mud pump brand.
Lake Petro has best processing & test equipments, which can undertake maintenance & repair services for each kind of mud pump.
Lake Petro has its own import & export License and formed its unique style sale network & service image and the products have been sold to United States, Mexico, Canada, British, German, Egypt, Nigeria, Russian, UAE etc.
|
No |
Properties |
Units |
Values |
Remark |
|
1 |
Composition |
% |
Y2O3+ZrO2≥99.5% |
ZrO2≥95% |
|
2 |
Density |
g/cm³ |
5.95-6.05 |
|
|
3 |
Flexural Strength |
Mpa |
800-1200 |
|
|
4 |
Tensile Strength |
Mpa |
500-600 |
|
|
5 |
Weibull Modulus |
M |
>30 |
|
|
6 |
Compressive Strength |
Mpa |
>1950 |
|
|
7 |
Modulus of Elasticity |
Gpa |
200 |
|
|
8 |
Poisson `s Ratio |
0.31 |
||
|
9 |
Hardness |
HV0.3kg/mm² |
>1120 |
HB≥87 |
|
10 |
Fracture Toughness |
Mpam¹/² |
8-10 |
|
|
11 |
Average Grain Size |
μm |
0.4-0.6 |
|
|
12 |
Thermal Conductivity |
W/m*K |
3.08 |
b). Double Metal Liner
Material for shell is forged steel pipe or seamless steel tube, 45#(ASTM1045). Normalizing hardness degree is 160BHN(HB180-200), percentage elongation 17%(δ>17%),tensile strength not less than 85000PSI(σb>610Mpa), Flexural Strength not less than 60000PSI(σb>450MPa)and shell with HP.
Sleeve material is high chrome centrifugal, which is chrome containing 26-28%, its thickness 0.25~0.35 inch (6.35 -8.89mm. its standard thickness is 7mm and special thickness reduced has 3 kinds, 4mm, 4.5mm & 5mm. Normally, it means standard thickness if there is no special explanation ), quenching hardness HRC59-67.
Its Chemical Composition Table is as following
|
Element |
C |
Cr |
Si |
Mn |
Mo |
S,P |
|
Content |
2.8%-3.1% |
26%-28% |
0.6%-0.9% |
0.5%-1% |
0.5%-0.8% |
<0.05% |
Some special chemical composition will be adopted to use on the sleeve according to the requirement of the client or special working conditions
c). High Frequency, Carburization & quenching Liner Material is 20#(ASTM1020)seamless steel tube or forged steel. The bore will be carburized first and then High Frequency quenching . The thickness of Carburized layer is more than 1.5mm and hardness of the bore is HRC58-62
d). Chrome-plated Liner
Material is 45#(ASTM1045)or 40Cr(ASTM5140)seamless steel tube or forged steel. Thickness of chrome plated is 0.15~0.2mm and hardness of Carburized layer is more than 1.5mm and hardness of the bore is HRC58-62